优势说明：PA66吸水量：每1%吸水量体积增加0.003in，在50%的相对湿度，23℃的气温吸水量是2.5%。收缩率为2.25%,比重1.14G/CM3详细说明:
1.PA66吸水量：每1%吸水量体积增加0.003in，在50%的相对湿度，23℃的气温吸水量是2.5%。收缩率为2.25%,比重1.14G/CM3
： 本公司可以免费提供各种材料认
证
| 产品说明 | |
| Vydyne® R513H BK Nylon resins are general purpose polyamide, 13% glass fiber reinforced, and heat stabilized resins. Available in natural and black. Ascend Performance Materials has engineering data available for this resin, including 50% RH data. Please contact your customer service representative. They are injection molding grade resins that are lubricated for machine feed, flow and mold release. Vydyne R513H is a member of a glass reinforced family supplied by Ascend Performance Materials which also includes 33% and 43% glass fiber loadings. These resins provide a range of cost performance products in which tensile strength is increased with the increasing glass fiber loadings. Glass reinforced Vydyne resins provide a higher heat distortion temperature, better resistance to creep, higher impact and better dimensional stability when compared with unreinforced Nylon 6,6. These products have good chemical resistance to a broad range of chemicals including many aliphatic and aromatic hydrocarbons found in most solvents, gasoline, hydraulic fluids, greases and machine oils. Vydyne R513H Series resins have tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption, and part weight are key advantages of Vydyne glass reinforced Nylon 6,6 resins over aluminum and/or zinc die cast parts. Vydyne R513H Series are heat stabilized and formulated to minimize the oxidative and thermal degradation of the nylon polymer when exposed to elevated temperatures for extended periods of time. Vydyne R513H provides improved retention of physical properties under exposure to long-term heat. The continuous operating use temperature is 275°F and short-term peak temperatures as high as 475°F. Typical Applications/End Uses: Vydyne R513H Series resins have been used for many under-the-hood automotive applications, motor housings for power tools, and garden appliances. These resins have also been used in miscellaneous brackets, gears, and clips, which require high rigidity and strength. | |
| 总体 | |
| 材料状态 | 已商用：当前有效 |
| 资料 1 | Processing （English）Technical Datasheet （English） |
| UL 黄卡 2 | E70062-249082 |
| 搜索 UL 黄卡 | Ascend Performance Materials LLC.Vydyne® |
| 供货地区 | 北美洲欧洲亚太地区 |
| 填料/增强材料 | 玻璃纤维增强材料, 13% 填料按重量 |
| 添加剂 | 热稳定剂润滑剂 |
| 性能特点 | 刚性，高高强度经润滑抗溶解性良好的流动性耐化学性良好耐汽油性耐油性能耐油脂性能热稳定性脱模性能良好 |
| 用途 | 齿轮动力/其它工具汽车的发动机罩下的零件型号 |
| 机构评级 | ASTM D 4066 PA012G15ASTM D 6779 PA012G15FED L-P-410AMIL M-20693B |
| UL 档案号 | E70062 |
| 外观 | 黑色自然色 |
| 形式 | 颗粒料 |
| 加工方法 | 注射成型 |
| 多点数据 | Isothermal Stress vs. Strain （ISO 11403-1） |
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 密度 | 1.22 | -- | g/cm3 | ISO 1183 |
| 收缩率 | ISO 294-4 | |||
| 横向流量: 73°F, 0.0787 in | 1.0 | -- | % | |
| 流量: 73°F, 0.0787 in | 0.50 | -- | % | |
| 吸水率 | ISO 62 | |||
| 73°F, 24 hr | 1.0 | -- | % | |
| 平衡, 73°F, 50% RH | 2.2 | -- | % |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 拉伸模量 （73°F） | 899000 | 566000 | psi | ISO 527-2 |
| 拉伸应力 （断裂, 73°F） | 17700 | 10900 | psi | ISO 527-2 |
| 拉伸应变 （断裂, 73°F） | 3.0 | 13 | % | ISO 527-2 |
| 弯曲模量 （73°F） | 754000 | 457000 | psi | ISO 178 |
| 弯曲强度 （73°F） | 29000 | 15400 | psi | ISO 178 |
| 泊松比 | 0.41 | -- | ISO 527-2 | |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | ISO 179 | |||
| -22°F | 3.8 | -- | ft·lb/in2 | |
| 73°F | 3.8 | -- | ft·lb/in2 | |
| 简支梁缺口冲击强度 | ISO 179 | |||
| -22°F | 17 | -- | ft·lb/in2 | |
| 73°F | 18 | -- | ft·lb/in2 | |
| 悬壁梁缺口冲击强度 （73°F） | 2.4 | -- | ft·lb/in2 | ISO 180 |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 热变形温度 | ||||
| 66 psi, 未退火 | 496 | -- | °F | ISO 75-2/B |
| 264 psi, 未退火 | 464 | -- | °F | ISO 75-2/A |
| 维卡软化温度 | 482 | -- | °F | ISO 306/B |
| 溶融温度（DSC） | 500 | -- | °F | ISO 3146 |
| 线形膨胀系数 | ISO 11359-2 | |||
| 流动: 73 到 131°F, 0.0787 in | 2.2E-6 | -- | in/in/°F | |
| 横向: 73 到 131°F, 0.0787 in | 6.1E-6 | -- | in/in/°F | |
| RTI Elec | UL 746 | |||
| 0.0280 in | 284 | -- | °F | |
| 0.0591 in | 284 | -- | °F | |
| 0.118 in | 284 | -- | °F | |
| RTI Imp | UL 746 | |||
| 0.0280 in | 248 | -- | °F | |
| 0.0591 in | 248 | -- | °F | |
| 0.118 in | 248 | -- | °F | |
| RTI Str | UL 746 | |||
| 0.0280 in | 257 | -- | °F | |
| 0.0591 in | 284 | -- | °F | |
| 0.118 in | 284 | -- | °F |
| 电气性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 体积电阻率 （0.118 in） | 4.0E+15 | -- | ohm·cm | IEC 60093 |
| 耐电强度 3 （73°F, 0.118 in） | 380 | -- | V/mil | IEC 60243-1 |
| 耐电弧性 （0.118 in） | PLC 6 | -- | ASTM D495 | |
| 相比耐漏电起痕指数（CTI） （0.118 in） | PLC 2 | -- | UL 746 | |
| 漏电起痕指数 （0.118 in） | 250 到 400 | -- | V | IEC 60112 |
| 高电弧燃烧指数（HAI） | UL 746 | |||
| 0.0280 in | PLC 0 | -- | ||
| 0.0591 in | PLC 0 | -- | ||
| 0.118 in | PLC 0 | -- | ||
| 高电压电弧起痕速率 （HVTR） （0.118 in） | PLC 1 | -- | UL 746 | |
| 热丝引燃 （HWI） | UL 746 | |||
| 0.0280 in | PLC 4 | -- | ||
| 0.0591 in | PLC 3 | -- | ||
| 0.118 in | PLC 4 | -- | ||
| 可燃性 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | |||
| 0.0280 in, All colors | HB | -- | ||
| 0.0591 in, All colors | HB | -- | ||
| 0.118 in, All colors | HB | -- | ||
| 灼热丝易燃指数 | IEC 60695-2-12 | |||
| 0.0280 in | 1250 | -- | °F | |
| 0.0591 in | 1250 | -- | °F | |
| 0.118 in | 1250 | -- | °F | |
| 热灯丝点火温度 | IEC 60695-2-13 | |||
| 0.0280 in | 1290 | -- | °F | |
| 0.0591 in | 1290 | -- | °F | |
| 0.118 in | 1290 | -- | °F | |
| 极限氧指数 | 25 | -- | % | ASTM D2863 |
| 注射 | 干燥 | 单位制 | |
| 干燥温度 | < 158 | °F | |
| 干燥时间 | 1.0 到 3.0 | hr | |
| 建议注入量 | 40 到 80 | % | |
| 建议的zui大回制料比例 | 25 | % | |
| 螺筒后部温度 | 536 到 590 | °F | |
| 螺筒中部温度 | 536 到 590 | °F | |
| 螺筒前部温度 | 536 到 590 | °F | |
| 射嘴温度 | 536 到 590 | °F | |
| 加工（熔体）温度 | 545 到 581 | °F | |
| 模具温度 | 149 到 203 | °F | |
| 注塑温度 | 7980 到 20300 | psi | |
| 注射速度 | 快速 | ||
| 保压 | 7980 到 20300 | psi | |
| 背压 | 29.0 到 145 | psi | |
| 螺杆转速 | 60 到 120 | rpm | |
| 合模力 | 1.9 到 4.5 | tons/in2 | |
| 垫层 | 0.118 到 0.252 | in | |
| 注射说明 | |||
| Injection Time: <1 to 2.5 sec |
:何生
:86-
传真号码:86-
地址:广东 东莞市
PA66美国首诺 R513H BK良好的流动性 耐化学性良好 耐汽油性其它产品
PA66美国首诺 R513H BK良好的流动性 耐化学性良好 耐汽油性
PA66美国首诺 R513H BK玻璃纤维增强材料, 13% 填料按重量
PA66美国首诺 R-220 矿物填料, 40% 填料按重量
PA66美国首诺 R-220齿轮 动力/其它工具
PA66美国首诺 R-220刚性，汽车外部零件 凸轮
PA66美国首诺 R-220刚性，高 抗溶解性 抗撞击性，良好 良好的强
PA66美国首诺 R-220热稳定性 韧性良好 延展性
PA66美国首诺 R-220耐化学性良好 耐汽油性 耐热性，高 耐油性能
PA66美国首诺 R350-GF25 玻璃纤维增强材料, 25%
PA66美国首诺 J350-GK30 玻璃珠, 30% 填料按重量