Romiloy 1035 F PC/ABS ROMIRA GmbH
Romiloy 1035 F PC/ABS ROMIRA GmbH
Romiloy 1035/04 GF 10 PC/ABS ROMIRA GmbH
Romiloy 1055 PC/ABS ROMIRA GmbH
Romiloy 1055 F PC/ABS ROMIRA GmbH
Romiloy 1035 F PC/ABS ROMIRA GmbH材料物性表如下:
| Physical | Nominal Value | Unit | Test Method |
| Density | 1.13 | g/cm3 | ISO 1183 |
| Melt Mass-Flow Rate （MFR） （260°C/5.0 kg） | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage （23°C） | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption （23°C, 24 hr） | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus （23°C） | 2150 | MPa | ISO 527-2/1 |
| Tensile Stress （Yield, 23°C） | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain （Break, 23°C） | 85 | % | ISO 527-2/50 |
| Flexural Modulus 2 （23°C） | 2200 | MPa | ISO 178 |
| Flexural Strength 2 （23°C） | 83.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Notched Impact Strength （23°C） | 38 | kJ/m2 | ISO 179/1eA |
| Charpy Unnotched Impact Strength （23°C） | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
| Heat Deflection Temperature （1.8 MPa, Unannealed） | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 121 | °C | ISO 306/B50 |
| CLTE - Flow （23 to 55°C） | 0.000085 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
| Flame Rating （1.60 mm） | HB | UL 94 |
| Additional Information |
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with DIN 16901. The value listed as Coefficient of Linear Thermal Expansion ISO 11359-1-2, was tested in accordance with DIN 53752. |
| Injection | Nominal Value | Unit | |
| Drying Temperature | < 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Processing （Melt） Temp | 240 to 270 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Extrusion | Nominal Value | Unit | |
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Cylinder Zone 1 Temp. | 210 to 250 | °C | |
| Cylinder Zone 2 Temp. | 210 to 250 | °C | |
| Cylinder Zone 3 Temp. | 210 to 250 | °C | |
| Cylinder Zone 4 Temp. | 210 to 250 | °C | |
| Cylinder Zone 5 Temp. | 210 to 250 | °C | |
| Melt Temperature | < 260 | °C |
Romiloy 1055 F PG PC/ABS ROMIRA GmbH
Romiloy 9150 PC/ABS ROMIRA GmbH
Romiloy 9170 PC/ABS ROMIRA GmbH
Rotec ABS TS 15/04 PC/ABS ROMIRA GmbH
:邓
:86-
传真号码:86-
地址:中国 广东 东莞 东莞市 樟木头镇 塑胶原料市场
Romiloy 1035 F PC/ABS ROMIRA原厂原包其它产品
Romiloy 1035 F PC/ABS ROMIRA原厂原包
Romiloy 1035 E PC/ABS ROMIRA原厂原包
Romiloy 1035 04 F PC/ABS ROMIRA原厂原包
Romiloy 1015 PC/ABS ROMIRA耐热性
RETAIN 8700 PC/ABS原厂原包
RETAIN 8660 PC/ABS原厂原包
RAMLLOY PBB701 PC/ABS Polyram抗紫外线
RAMLLOY PBB520 PC/ABS Polyram阻燃
RAMLLOY PBB503 PC/ABS Polyram阻燃
RAMLLOY PBB106 PC/ABS Polyram抗紫外线