产品用途:汽车底盘ABS线束应用
序号 | Description规格 | Tolerance(mm) 内外径公差 | Wall thickness(mm) 壁厚 | Tolerance wall thickness(mm) 壁厚公差 |
1 | PUR1.6*3mm | ±0.15 | 0.7 | ± 0.15 |
2 | PUR3*5mm | ±0.15 | 1.0 | ± 0.15 |
3 | PUR3.5*6.1mm | ±0.15 | 1.3 | ±0.15 |
4 | PUR4*6mm | ±0.15 | 1.0 | ± 0.15 |
5 | PUR4.5*7.1.mm | ±0.15 | 1.3 | ± 0.15 |
6 | PUR5*6mm | ±0.15 | 0.5 | ± 0.15 |
7 | PUR5*8mm | ±0.3 | 1.5 | ± 0.15 |
8 | PUR6*7mm | ±0.3 | 0.5 | ± 0.15 |
9 | PUR6*8.6mm | ±0.3 | 1.3 | ± 0.15 |
10 | PUR6*9mm | ±0.3 | 1.5 | ± 0.15 |
11 | PUR6.5*9mm | ±0.3 | 1.25 | ± 0.15 |
12 | PUR6.5x9.7mm | ±0.3 | 1.6 | ± 0.15 |
13 | PUR7*9.7mm | ±0.3 | 1.35 | ± 0.15 |
14 | PUR7*10mm | ±0.3 | 1.5 | ± 0.15 |
15 | PUR7*10.7mm | ±0.3 | 1.85 | ± 0.15 |
16 | PUR7.5*10.1mm | ±0.3 | 1.3 | ± 0.15 |
17 | PUR7.5*10.7mm | ±0.3 | 1.6 | ± 0.15 |
18 | PUR8.0*10.7mm | ±0.3 | 1.35 | ± 0.15 |
19 | PUR8.5*11.1mm | ±0.3 | 1.3 | ± 0.15 |
20 | PUR9**10.4mm | ±0.3 | 0.7 | ± 0.15 |
21 | PUR9*12mm | ±0.3 | 1.5 | ± 0.15 |
22 | PUR10*12.7mm | ±0.3 | 1.35 | ± 0.15 |
23 | PUR10.1*11.3mm | ±0.3 | 0.6 | ± 0.15 |
24 | PUR13*5.7mm | ±0.3 | 1.35 | ± 0.15 |
Description 性能 | Test Method 测试方法 | 判定标准 Typical value |
Shore A hardness 邵氏硬度A | DIN ISO 7619-1(3S) | 85(+/-5) |
Tensile strength, 拉伸强度 | TL 529-2008 1 6.2 & DIN 53504:2009 | ≥30N/mm2 |
Dimension change rate, 尺寸变化率 | ES-2U5A-1A263-AA-2005 6.4 ,170℃,24h | ≤10% |
Abrasion, mm3 耐磨损 | ES-2U5A-1A263-AA-2005 6.9 &ASTM D4060-2014 | ≤0.1% |
Flammability 燃烧测试 | ES-2U5A-1A263-AA-2005 6.10 & ISO 3795:1989 | ≤100mm/min |
Low temperature resistance 耐低温 | ES-2U5A-1A263-AA-2005 6.5 ,-40℃,4h | No deformation and no break 无变形或开裂 |
High temperature 高温测试 | GB/T2423.1-2008 | No deformation and no break |
Temperature resistance 耐热性能 | ES-2U5A-1A263-AA-2005 6.8 ,125℃,3000h | No deformation and no break 无变形或开裂 |
Thermal aging test 热老化测试 | ES-2U5A-1A263-AA-2005 6.3 ,125℃,400h | ≥35% |
Odor 气味 | Refer FLTM BO 131-03 (2017) Sampling volume:3L,type:A ,Size:100cm² | WSS-M99P2222-F1 (2017) ≤3.0 |
VOC | Refer FLTM BZ 108-01( 7/2/2018)VOC, (HPLC/DAD) (TDS/GC-MS) | / |
Nebulization 雾化 | Refer SAE J1756(2006) Reflection method :heating at 100 ℃ /3 hours . condensing temperature 21℃,Drying time 16 hours | Based on WSS-M99P2222-F1(2017) Reflection method 反射法:≥70,无油膜、液滴、结晶状沉积物 |
Density 密度 | TL 529-2008 1&DIN EN ISO 1183-1:2013 Method A | 1.095g/cm3 |
ELV | GB/T 30512-2014 | 铅(Pb)≤100ppm、镉(Cd)、汞(Hg)、六价铬(Cr6+)、多溴联苯(PBBs)、多溴二苯醚(PBDEs)≤1000ppm |
RoHS | Refer RoHS Directive2011/65/EU and amending Annex directive EU 2015/863 | 铅(Pb)≤100ppm、 镉(Cd)、汞(Hg)、六价铬(Cr6+)、多溴联苯(PBBs)、多溴二苯醚(PBDEs)、DBP、BBP、DEHP、DIBP≤1000ppm |
Short term aging 短期老化 | ISO 6722-1:2011 150 ℃,240 h→-25℃,4h | No crack and no break |
Elongation at break 断裂伸长率 | TL 529-2008 1 6.2 & DIN 53504:2009 | ≥400% |
IR 红外光谱 | GB/T 6040-2019 | ≥95% |
Impact test抗冲击试验 | ISO 6722-2011 | No crack and no break |
Ozone resistance 耐臭氧试验 | SMTC 3 261 004 | '0 level , No crack |
Chemical resistance 耐化学试剂 | SMTC 3 800 001-20109(V1) 10.2 | No break |
Hydrolysis resistance 耐水解 | 500h storage in istilled water at 85℃ for 500h 85℃蒸馏水中存放 | No crack and no break |
Crushed stone impact test碎石冲击试验 | SAE J400-2012 | No break and no scratch on the tube surface 套管表面无明显损坏、磨痕 |