美国SABIC LEXAN PC DMX1132*价格
LEXAN ? Resin DMX1132 | SI | | British | | Metric | Americas: OBSOLETE |
LEXAN DMX1132 is a high flow polycarbonate copolymer resin with improved ammonia resistance over regular polycarbonate resin. |
美国SABIC LEXAN PC DMX1132*价格
Property |
TYPICAL PROPERTIES (1) | ||||
MECHANICAL | Value | Unit | Standard | |
Tensile Stress, yld, Type I, 50 mm/min | 700 | kgf/cm2 | ASTM D 638 | |
Tensile Stress, brk, Type I, 50 mm/min | 560 | kgf/cm2 | ASTM D 638 | |
Tensile Strain, yld, Type I, 50 mm/min | 7 | % | ASTM D 638 | |
Tensile Strain, brk, Type I, 50 mm/min | 50 | % | ASTM D 638 | |
Tensile Modulus, 5 mm/min | 26000 | kgf/cm2 | ASTM D 638 | |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1120 | kgf/cm2 | ASTM D 790 | |
Flexural Modulus, 1.3 mm/min, 50 mm span | 25500 | kgf/cm2 | ASTM D 790 | |
Tensile Stress, yield, 50 mm/min | 73 | MPa | ISO 527 | |
Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 | |
Tensile Strain, yield, 50 mm/min | 7 | % | ISO 527 | |
Tensile Strain, break, 50 mm/min | >25 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 | |
Flexural Stress, yield, 2 mm/min | 100 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 | |
Hardness, H358/30 | 110 | MPa | ISO 2039-1 | |
Pencil Hardness test, 1kgf | HB | - | ASTM D 3363 | |
Erichson scratch depth, 6N | 17 | micrometer | SABIC Method | |
IMPACT | Value | Unit | Standard | |
Izod Impact, notched, 23°C | 1 | cm-kgf/cm | ASTM D 256 | |
Instrumented Impact Total Energy, 23°C | 734 | cm-kgf | ASTM D 3763 | |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U | |
Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U | |
Izod Impact, notched 80*10*3 +23°C | 5 | kJ/m2 | ISO 180/1A | |
Izod Impact, notched 80*10*3 -30°C | 3 | kJ/m2 | ISO 180/1A | |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 3 | kJ/m2 | ISO 179/1eA | |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 5 | kJ/m2 | ISO 179/1eA | |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU | |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 90 | kJ/m2 | ISO 179/1eU | |
THERMAL | Value | Unit | Standard | |
Vicat Softening Temp, Rate B/50 | 137 | °C | ASTM D 1525 | |
HDT, 0.45 MPa, 3.2 mm, unannealed | 132 | °C | ASTM D 648 | |
HDT, 1.82 MPa, 3.2mm, unannealed | 121 | °C | ASTM D 648 | |
CTE, -40°C to 95°C, flow | 7.E-05 | 1/°C | ASTM E 831 | |
CTE, -40°C to 95°C, xflow | 7.E-05 | 1/°C | ASTM E 831 | |
Thermal Conductivity | 0.2 | W/m-°C | ASTM C 177 | |
Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 | |
CTE, 23°C to 80°C, flow | 7.E-05 | 1/°C | ISO 11359-2 | |
CTE, 23°C to 80°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 | |
Vicat Softening Temp, Rate B/50 | 140 | °C | ISO 306 | |
Vicat Softening Temp, Rate B/120 | 141 | °C | ISO 306 | |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 133 | °C | ISO 75/Bf | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af | |
PHYSICAL | Value | Unit | Standard | |
Specific Gravity | 1.2 | - | ASTM D 792 | |
Density | 1.19 | g/cm3 | ASTM D 792 | |
Mold Shrinkage, flow, 3.2 mm (5) | 0.6 - 0.8 | % | SABIC Method | |
Mold Shrinkage, xflow, 3.2 mm (5) | 0.6 - 0.8 | % | SABIC Method | |
Melt Flow Rate, 300°C/1.2 kgf | 38.5 | g/10 min | ASTM D 1238 | |
Density | 1.19 | g/cm3 | ISO 1183 | |
Melt Volume Rate, MVR at 300°C/1.2 kg | 36 | cm3/10 min | ISO 1133 | |
OPTICAL | Value | Unit | Standard | |
Refractive Index | 1.586 | - | ASTM D 542 | |
Refractive Index | 1.586 | - | ISO 489 |
Source GMD, last updated:2008/04/02 |
Processing |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 120 | °C |
Drying Time | 3 - 4 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 295 - 315 | °C |
Nozzle Temperature | 290 - 310 | °C |
Front - Zone 3 Temperature | 295 - 315 | °C |
Middle - Zone 2 Temperature | 280 - 305 | °C |
Rear - Zone 1 Temperature | 260 - 280 | °C |
Hopper Temperature | 60 - 80 | °C |
Mold Temperature | 70 - 95 | °C |